1. Defect Formation during Solidification in Grey Iron Castings
Abstract : The presence of defects is of major concern in the production of grey iron castings. Some defects are merely an aesthetic problem while others can be detrimental for the performance of the component. Among the several possible defects, shrinkage porosity is one of the more challenging to understand and avoid. READ MORE
-
2. The mechanisms of metal expansion penetration during solidification of grey cast iron
Abstract : The production of high quality castings requires the casting surface to be clean and free from defects. One type of defect often found is caused by metal penetration into the sand mould. READ MORE
-
3. Factors Influencing the Formation of Shrinkage Porosity in Grey Cast Iron
Abstract : The presence of shrinkage defects is of major concern in the production of grey iron castings. This type of defect can penetrate through the casting as a three-dimensional network. READ MORE