Search for dissertations about: "crack"

Showing result 11 - 15 of 538 swedish dissertations containing the word crack.

  2. 11. Fatigue of Spot Welded Joints: Experiments and Life Predictions

    Author : Hans-Fredrik Henrysson; Chalmers tekniska högskola; []
    Keywords : TEKNIK OCH TEKNOLOGIER; ENGINEERING AND TECHNOLOGY; crack closure; crack propagation; crack initiation; finite element method; damage accumulation; variable amplitude; fracture mechanics; fatigue; spot welds;

    Abstract : Methods to assess the fatigue strength of spot welds in built-up structures are used on a daily basis in the automotive industry. Efficient and reliable numerical methods make it possible to achieve designs with low weight, low manufacturing costs and good durability within short development cycles, since the number of prototypes built can be reduced. READ MORE

  4. 12. Contact fatigue and crack propagation studies of sintered PM steel

    Author : Anders Holmberg; Åsa Kassman Rudolphi; Urban Wiklund; Johan Ahlström; Uppsala universitet; []
    Keywords : TEKNIK OCH TEKNOLOGIER; ENGINEERING AND TECHNOLOGY; Tribology; PM steel; Fatigue; Crack Initiation; Crack Propagation; Material Analysis; Teknisk fysik med inriktning mot tribomaterial; Engineering Science with specialization in Tribo Materials;

    Abstract : Gears made of PM steel are of interest for the automotive industry because from the press/sinter route, complex geometries can be produced to near net shape with only a few processing steps while keeping the material and energy usage at a minimum. However, the PM steels of today have significant performance limitations caused by the inherent porosity which impairs the mechanical properties by acting as stress raisers in the material. READ MORE

  5. 13. Failure of thermal barrier coatings under thermal and mechanical fatigue loading : microstructural observations and modelling aspects

    Author : Håkan Brodin; Anette M. Karlsson; Linköpings universitet; []
    Keywords : thermal barrier coating; TBC; delamination; crack initiation; crack propagation; crack growth; oxidation; alumina; spinel; MCrAIY; diffusion; fatigue; modelling; modeling; degradation; TECHNOLOGY; TEKNIKVETENSKAP;

    Abstract : Industrial and air-borne gas turbine hot components suffer from creep, oxidation, corrosion and microstructural degradation if not shielded from the hot and aggressive combustion gases. Two major strategies commercially available are adopted; film cooling by pressurised air and application of protective coatings. READ MORE

  6. 14. Thermo-mechanical Fatigue Crack Propagation in Inconel 718

    Author : Lars Jacobsson; Materialteknik; []
    Keywords : TEKNIK OCH TEKNOLOGIER; ENGINEERING AND TECHNOLOGY; crack closure; image analysis; potential drop; in-situ scanning elecron microscopy; crack propagation experiments; Thermo-mechanical fatigue; Inconel 718;

    Abstract : Thermo-mechanical fatigue crack propagation in Inconel 718 has been studied with different methods. In-situ observations with a scanning electron microscope (SEM) were performed, the crack propagation process was followed cycle by cycle and the influences from load, temperature, and microstructure on the crack growth were analyzed. READ MORE

  7. 15. On the hot crack formation during solidification of iron-base alloys

    Author : Karin Hansson; KTH; []
    Keywords : hot cracking; hot tearing; cracking fracturing ; tearing; ductility; brittleness; embrittlement; fractures; ductile brittle transition; solidification; iron; copper; nickel; Invar; steels; free machining steels; stainless steels; penetration; crack;

    Abstract : Hot cracking during solidification is a severe problem inmany casting processes, for example in continuous casting.Combinations of low strength and low ductility of the materialat high temperatures and applied tensile stress can cause hotcracking. READ MORE