6. Non-destructive measurement of near-surface cracks in railheads : with focus on ultrasonic inspections
Abstract : Near-surface cracks in railhead that caused by rolling contact fatigue (RCF) is one of a kind rail defects that degrade rail track quality. Dependent on the trail load, the cracks can reach to severe level quickly. READ MORE
-
7. Life Prediction and Mechanical Behavior of Thermal Barrier Coatings
Abstract : Delamination and spallation of thermal barrier coating (TBC) systems, used in hot parts of gas turbines, have been studied with respect to thermal fatigue. TBCs with and without pre-existing cracks were investigated. Thermal shock tests were performed until coating spallation. READ MORE
-
8. Closed-die forging and slab hot rolling with focus on material yield : some industrial problems analysed by FEM
Abstract : The thesis is focussed on improving the material yield in closed-die forging and rolling. The former is restricted to the manufacturing of heavy crown wheels and front axle beams and the latter to the hot rolling of steel slabs. To enhance the yield the commercial FE-codes Form2D and Dyna3D are used. READ MORE
-
9. Steel fibre corrosion in cracks : durability of sprayed concrete
Abstract : Steel fibre reinforced sprayed concrete is common practice for permanent linings in underground construction. Today there is a demand on "expected technical service life" of 120 years. Thin steel fibres could be expected to discontinue carrying load fast with a decrease of fibre diameter caused by corrosion, especially in cracks. READ MORE
-
10. Durability of sprayed concrete : steel fibre corrosion in cracks
Abstract : A combination of sprayed concrete technique and steel fibre technology gives obvious advantages when saving the work needed to place conventional reinforcement. In rock strengthening applications this is most accentuated. Sprayed concrete in general, made by skilled workmen, will generally be of high quality and good durability. READ MORE