Search for dissertations about: "fatigue test"
Showing result 1 - 5 of 218 swedish dissertations containing the words fatigue test.
-
1. Oxidation, Creep and Fatigue Synergies in Cast Materials for Exhaust Manifolds
Abstract : The future development of engines of heavy-duty vehicles towards reduced CO2 emission will increase the exhaust gas temperature and render the exhaust atmosphere more corrosive. The current service material of exhaust gas components - a ferritic ductile cast iron called SiMo51 - will soon meet its upper-temperature limit. READ MORE
-
2. Fatigue of Asphalt Mixes - Theory of Viscoelasticity and Continuum Damage Mechanics Applied to Uniaxial Fatigue Data from Laboratory Tests
Abstract : The advance of analytic (mechanistic) design methods increases the need for fundamental material properties. Fatigue cracking due to traffic loading, in combination with permanent deformation (rutting), thermal cracking, irregularities, frost heave and reflective cracking are some of the major criteria used when designing an asphalt concrete pavement. READ MORE
-
3. Fatigue strength of engineering materials : the influence of environment and porosity
Abstract : The objective of this work was to use LEFM in order to assess the detrimental influence of surrounding chloride-containing environments for stainless steels, hardened steel as well as for a cast aluminium alloy. An additional aim was also to use LEFM to assess the influence of porosity on the fatigue properties for different commercial cast aluminium alloys and manufacturing methods. READ MORE
-
4. High Temperature Fatigue Behaviour of Austenitic Stainless Steel : Microstructural Evolution during Dwell-Fatigue and Thermomechanical Fatigue
Abstract : The global energy consumption is increasing and together with global warming from greenhouse gas emission, a need for more environmentally friendly energy production processes is created. Higher efficiency of biomass power plants can be achieved by increasing temperature and pressure in the boiler section, this would increase the generation of electricity along with the reduction in emission of greenhouse gases e. READ MORE
-
5. Very high cycle fatigue of automotive steels : Testing and computation at 20 kHz
Abstract : Mechanical fatigue failure occurs in components subjected to cyclic loading. A crack initiates at critical regions in the component and propagates during repeated loading. The expected fatigue life depends on the level, type and frequency of the loading. READ MORE