  1. 1. Metal Expansion Penetration During Solidification of Grey Cast Iron

    Author : Izudin Dugic; Linköpings universitet; []
    Keywords : TEKNIK OCH TEKNOLOGIER; ENGINEERING AND TECHNOLOGY; Grey cast iron; solidification; solidification modelling; graphite expansion; molar volume; casting simulation; thennal analysis; thermoanalysis cup; casting temperature; inoculation; inoculant; meta! expansion penetration; eutectic cell size.; TECHNOLOGY; TEKNIKVETENSKAP;

    Abstract : The meta! expansion penetration has been examined experimentally. The whole casting process was simulated using a commercial software, in order to investigate the solidification characteristics and the pore formation in the casting studied. READ MORE

  2. 2. Rapid solidification behaviour of Fe and Al based alloys

    Author : Sathees Ranganathan; Hasse Fredriksson; Zhongyun Fan; KTH; []
    Keywords : TEKNIK OCH TEKNOLOGIER; ENGINEERING AND TECHNOLOGY; Rapid solidification; Melt spinning; Metastable phases; Fe based alloys.; Metallurgical process and manufacturing engineering; Metallurgisk process- och produktionsteknik;

    Abstract : Rapid solidification experiment on Fe-Cr-Mo-Mn-Si-C alloy was performed to investigate metastable phases formed during the solidification. A wide range of cooling rate was used to analyse the sample from melt spinning technique (~107 K/s) to water quenching method (~102 K/s). READ MORE

  3. 3. On the solidification of compacted and spheroidal graphite irons

    Author : Björn Domeij; Attila Diószegi; Jönköping University; []
    Keywords : TEKNIK OCH TEKNOLOGIER; ENGINEERING AND TECHNOLOGY; Compacted graphite iron; Spheroidal graphite iron; Solidification; Microsegregation; Kompaktgrafitjärn; segjärn; stelning; mikrosegregation;

    Abstract : A good understanding of the solidification process of a cast material is essential to understand how the combination of alloy composition and the casting process variables combines into the solid cast component and its performance. The wrong combination may result in poor performance or casting defects. READ MORE

  4. 4. Development of microstructure in cast magnesium alloys

    Author : Liu-Ying Wei; Chalmers tekniska högskola; []
    Keywords : NATURVETENSKAP; NATURAL SCIENCES; solidification behaviour; precipitation;

    Abstract : .... READ MORE

  5. 5. Stabilization-solidification of high water content dredged sediment : Strength, compressibility and durability evaluations

    Author : Gregory Makusa; Kauko Kujala; Luleå tekniska universitet; []

    Abstract : Dredging activities at ports and harbors are inevitable for safe navigation of ships and vessels. The outcomes of dredging are huge volumes of dredged materials, which can range from very fine and contaminated sediments to sands and gravels. The coarse sands and gravels can be directly used in civil engineering applications. READ MORE