1. Fatigue of existing steel bridges : Reliability and risk analyses for decision-making
Abstract : Fatigue is one of the primary reasons that limit the service life of steel bridges. Many bridges in Sweden and other countries have progressively approached their anticipated service lives. Since funding and resources are limited, simultaneously replacement or maintenance of bridges is impractical. READ MORE
-
2. Refining the fatigue assessment procedure of existing steel bridges
Abstract : This thesis treats the fatigue assessment process of steel bridges. The purpose is to identify areas with potential of enhancement with an overall aim of attaining a longer service life. The aging bridge stock in Sweden and in many other developed countries is an impending economical burden. READ MORE
-
3. Reliability-based fatigue assessment of existing steel bridges
Abstract : Fatigue is among the most critical forms of deterioration damage that occurs tosteel bridges. It causes a decline of the safety level of bridges over time. Therefore,the performance of steel bridges, which may be seriously affected by fatigue, shouldbe assessed and predicted. READ MORE
-
4. Innovative structural details using high strength steel for steel bridges
Abstract : The use of high strength steel has the potential to reduce the amount of steel used in bridge structures and thereby facilitate a more sustainable construction. The amount of steel and what steel grade that can be used in bridge structures and other cyclic loaded structures are often limited by a material degradation process called fatigue. READ MORE
-
5. Fatigue of steel bridges : New structural details and the implementation of high strength steel
Abstract : The use of high strength steel has the potential to reduce the amount of steel used in bridge structures and thereby facilitate a more sustainable construction. The amount of steel and what steel grade that can be used in bridge structures and other cyclic loaded structures are often limited by a material degradation process called fatigue. READ MORE