6. Surface integrity and corrosion behavior of stainless steels after grinding operations
Abstract : Stainless steels are widely used in applications where both the mechanical properties of steels and high corrosion resistance are required. There is continuous research to enable stainless steel components to be produced in a more economical way and be used in more harsh environments. READ MORE
-
7. Strain-assisted corrosion cracking and growth rate inhibitors
Abstract : A model for evolution of cracks as a result of strain-assisted corrosion is presented. The considered cracks possess a realistic geometry, where the tip region is an integral part of the crack surface instead of being a singular point. This geometry is either implicitly defined or is a consequence of crack nucleation from surface irregularities. READ MORE
-
8. Corrosion testing of heat exchanger tubing
Abstract : Heat exchanger tubes are commonly made from stainless steel.In a heat exchanger both the process fluid and the cooling orheating media can be corrosive. It is therefore important to beable to select materials that do not suffer from corrosion.Current methods in this area, however, suffer from limitationsand shortcomings. READ MORE
-
9. Influence of grinding operations on surface integrity and chloride induced stress corrosion cracking of stainless steels
Abstract : Stainless steels were developed in the early 20th century and are used where both the mechanical properties of steels and corrosion resistance are required. There is continuous research to allow stainless steel components to be produced in a more economical way and be used in more harsh environments. READ MORE
-
10. 2D hybrid modeling of defects in an ultrasonic inspection situation
Abstract : Advanced methods of nondestructive evaluations (NDE) are widely used for in-service inspection in many industrial applications, e.g. nuclear and aerospace industries. In these applications the components are exposed to different degradation mechanisms (e. READ MORE