16. The mechanisms of metal expansion penetration during solidification of grey cast iron
Abstract : The production of high quality castings requires the casting surface to be clean and free from defects. One type of defect often found is caused by metal penetration into the sand mould. READ MORE
-
17. The Effect of Processing Parameters and Alloy Composition on the Microstructure Formation and Quality of DC Cast Aluminium Alloys
Abstract : The objective of this research is to increase the understanding of the solidification behaviour of some industrially important wrought aluminium alloys. The investigation methods range from direct investigations of as-cast ingots to laboratory-scale techniques in which ingot casting is simulated. READ MORE
-
18. Microstructural Characterization of Expanded Austenite in 304L and 904L Austenitic Stainless Steels
Abstract : Austenitic stainless steels are among the most used materials in modern industry, mainly because of their superior corrosion resistance. However, low hardness and poor tribological properties often restrict their applicability. READ MORE
-
19. Assessment and improvements of thermal-hydraulic correlations and methods for the analysis of the Jules Horowitz Reactor
Abstract : Nuclear research reactors are used to test materials for current and future nuclear technologies, and to produce radioisotopes for medical purposes. Most of the existing Material Testing Reactors in Europe have operated for more than 50 years and new ones are needed. READ MORE
-
20. Comprehensive numerical analysis of stress state in adhesive layer of joint including thermal residual stress and material non-linearity
Abstract : The main objective of this work is to improve understanding of the stress state in the adhesive layer of bonded joints and identify key parameters which govern performance of adhesive joints. This information is crucial for the prediction of the failure initiation and propagation with the further estimation of the durability and strength of adhesively bonded structures. READ MORE