On the influence of Si on anodising and mechanical properties of cast aluminium alloys

Abstract: The combination of two cost-effective processes, i.e. casting and anodising, would be an interest for the aluminium component applications. However, there are some obstacles in the application of anodising on cast Al alloys. The challenges mostly relate to the alloying elements especially Si and the surface quality. With the development of casting process, cast aluminium alloys with low Si content can be casted, and a complex geometry component with reasonably good surface finish can be achieved. This study aims to identify the influence of Si on anodising and mechanical properties of Al-Si alloys.In this study, six Al-Si alloys with three different Si level and two different Sr level were investigated. Sr acts as a modifier to change the morphology of Si particles. The directional solidification technology was used to vary the microstructure coarseness by controlling the cooling rate to study the influence of Si level, Si particle morphology and cooling rate on mechanical properties, oxide layer formation and corrosion protection performance in cast Al-Si alloys.This study has observed that Si has a significant influence on anodising. During anodising, Si particles are anodised at a lower rate than the Al phase. The presence of Si particles in eutectic phase make the oxide layer locally thinner and more defected due to the low oxide growth rate in eutectic phase. This study observed the presence of residual metallic Al phase beneath or between Si particles. Due to their presence and their geometry, Al can be shielded by Si particles and prevented from oxidation. Si particles also act as a key role in the corrosion protection of oxide layer in Al-Si alloys. The corrosion attack propagates along Si particles as well as oxide defects to the Al substrate.It is found that the morphology of Si particles has a significant influence on the oxide layer formation and corrosion protection performance of the oxide layer on cast Al-Si alloys. A substantially improvement the corrosion resistance of anodised layer on Al-Si alloys is attributed to the morphology change from interconnected flakes to disconnected Si fibres when Sr is added, with less oxide defects and better oxide distribution.The Si level governs the mechanical properties of Al-Si based alloys. An increase of Si content in Al alloys improves the mechanical properties such as ultimate tensile and yield strength as well as hardness of the materials, but decreases the ductility. However, an increase of Si level in Al alloys decreases the thickness of oxide layer, and thereby, the corrosion protection of the oxide layer is deteriorated.