Imperfections in Recycled Aluminium-Silicon Cast Alloys

Abstract: In striving to produce high quality cast components from recycled aluminium alloys,imperfections have to be considered, because recycled aluminium usually containsmore of it. However, there are great energy savings to be made by using recycledaluminium; as little as 5% of the energy needed for primary aluminium productionmay be required. High quality castings are dependent on, besides alloy chemistry, bothmelt quality and the casting process; the focus of this work is related to the meltquality.This thesis aims to increase knowledge about imperfections, foremost about Fe-richparticles, oxides/bifilms, and porosity. Experiments were performed at industrialfoundry facilities and in a laboratory environment. Melt quality was evaluated byproducing samples with the reduced pressure test (RPT), from which both densityindex (DI) and bifilm index (BI) could be measured, results that were related to tensiletest properties. Data from tensile test samples were analysed, and fracture surfacesand cross sections were studied in both light microscope and in scanning electronmicroscope (SEM). For the purpose of investigating nucleation of primary Fe-richparticles (sludge) differential scanning calorimetry (DSC) was used.In the analysis of results, a correlation between the morphology of particles and tensileproperties were found. And elongated Fe-rich β-particles were seen to fracturethrough cleavage towards the centre. However, DI and BI have not been possible torelate to tensile properties.The nucleation temperature of primary Fe-rich particles were found to increase withincreased Fe, Mn, and Cr contents, i.e. the sludge factor (SF), regardless of cooling rate.For a set SF, an increase of cooling rate will decrease the nucleation temperature.