1. High Strain Fatigue Crack Growth and Crack Closure
Abstract : Understanding of the growth of fatigue cracks is of utmost importance since such growth often has a profound influence on the life of components subjected to cyclic loading. Thus, reliable fatigue life models enable a more efficient use of materials and improve the performance and efficiency in many applications. READ MORE
-
2. Modelling of TMF Crack Growth in Polycrystalline Gas Turbine Alloys : Accounting for Crack Closure Effects
Abstract : The main objective of the work presented in this Licentiate of Engineering thesis is to investigate and model the fatigue crack propagation behaviour of the nickel-based superalloy Inconel 792, with special attention to the industrial lifing of high-temperature components. In-phase (IP) crack propagation tests have been performed at different temperatures and loading regimes, including extended hold times. READ MORE
-
3. Rolling Contact Fatigue of Railway Rails with Emphasis on Crack Initiation
Abstract : Increased traffic density and the heavier axle loads of modern trains have led to severe problems with rolling contact fatigue (RCF) which cause initiation of surface cracks in railheads. In this thesis, a specific type of surface crack, the head check, is studied numerically with emphasis on fatigue crack initiation. READ MORE
-
4. Fatigue of Spot Welded Joints: Experiments and Life Predictions
Abstract : Methods to assess the fatigue strength of spot welds in built-up structures are used on a daily basis in the automotive industry. Efficient and reliable numerical methods make it possible to achieve designs with low weight, low manufacturing costs and good durability within short development cycles, since the number of prototypes built can be reduced. READ MORE
-
5. Thermo-mechanical Fatigue Crack Propagation in Inconel 718
Abstract : Thermo-mechanical fatigue crack propagation in Inconel 718 has been studied with different methods. In-situ observations with a scanning electron microscope (SEM) were performed, the crack propagation process was followed cycle by cycle and the influences from load, temperature, and microstructure on the crack growth were analyzed. READ MORE