High strength paper from high yield pulps by means of hot-pressing

Abstract: AbstractHigh Yield Pulp (HYP), i.e. TMP, SGW or CTMP, is normally used in printing papers (News, SC and LWC) or in a middle layer on cardboard i.e. in products that either have high demands on printability and runnability in fast printing presses or contribute to high bulk in cardboards in order to minimize pulp consumption at a certain sheet stiffness. Tensile strength as a function of density is significantly higher for HYP compared to chemical pulps such as sulphate and sulphite pulps. However, chemical pulp is mainly used in packaging materials that require very high tensile strength, while at the same time allowing the density of the paper to be high. By utilizing the softening properties of high-yielding lignin-rich fibres by hot-pressing technology, it is possible to significantly increase sheet density and thereby strength closer to the level of chemical pulps. Furthermore, due to the presence of high levels of lignin, it was shown that considerably higher wet strength can be achieved compared to chemical pulp without the addition of strengthening agents. The study focuses on the softening of stiff and lignin-rich fibres in papers based on HYP with sufficiently high moisture contents, when hot-pressing at temperature levels significantly above the softening temperature (Tg) of lignin Hot-pressing increases the density of the sheet which increases the contact surface between the fibres in the paper structure. The high pressing temperature can be said to induce a viscous flow of lignin, which also increases the potential for fibre-fibre bonding. It is conceivable that covalent bonds are obtained via condensation reactions and partly that interdiffusion between the lignin in the fibre walls can be obtained as they come close enough to each other during the hot-pressing. The research also shows that hot-pressing greatly improves properties in the form of dry and wet strength as well as hydrophobicity for HYP and for lignin-rich kraft paper. The first part of the study shows the effect of hot-pressing on strength properties of paper sheets based on CTMP, HT-CTMP, TMP, NSSC, SCPal and NBSK. The second part includes a study on how and to what extent different amounts of residual lignin in the pulp contribute to the dry and wet strength of the sheets of paper during hot-pressing as a function of increasing temperature. To demonstrate this, pilot scale cooking of unbleached pulp to various lignin levels was carried out. In all experiments in parts one and two, laboratory sheets with a surface weight of 150 g/m2 and a dry content of 50% were made with a Rapid Köthen (RK) sheet former, after which the sheets were hot-pressed in a cylinder press at temperatures up to 200°C, constant high pressure of about 7 MPa, nip pressure dwell time of 1.5 sec and production speed 1 m/min. The third part includes a study on the optimization of variables in a new design of a dynamic cylinder press for hot-pressing technology. This design is based on previous research at Mid Sweden University combined with key knowledge of steel band technology within IPCO AB. The new pilot machine is based on heating of a steel belt with infrared heat (IR) up to 300°C, a maximum line load of 15 kN/m in two press nips and a dwell time of 23-240 ms in the nip depending on the production speed which is up to 5 m/min. The experiments in part three were based on RK paper sheets with 100 g/m2 and approximately 63% dry content made by HT-CTMP. The results confirm that hot-pressed HYP-based paper sheets enable permanent densification by softening lignin, which provides a very high dry tensile strength and a remarkable improvement in wet tensile strength compared to bleached kraft pulp without the need for wet strength agents. A tensile index of 75 kNm/kg, compression strength index (SCT) of 45 kNm/kg and wet tensile strength index of 16 kNm/kg were obtained, which can be compared with the corresponding values for bleached kraft pulp based paper sheets of 85 kNm/kg, 35 kNm/kg and 5 kNm/kg respectively, all with the same density after hot-pressing at 200°C. The NSSC reached the highest tensile strength index of 92 kNm/kg. The study with the unbleached kraft pulps showed that the lignin content had a significant effect on both the dry and wet tensile strength indices. The pulps showed a linear relationship between wet strength and lignin content. The increase in lignin content from 0% to 12% improved the dry tensile index by 20% and SCT by 35% and gave a very significant increase in the wet strength index from 3 to 23 kNm/kg after hot-pressing. All lignin-rich paper samples exhibit good wet stability for at least 24 hours and an improved surface hydrophobicity by increasing the pressing temperature and lignin content.Optimization of the new steel belt based press machine showed that high nip pressure and two press nips had a great effect on density and strength. Whereas high temperature, well above Tg of lignin, and long pressing time were more important to achieve high wet strength. The highest wet strength index value, 27 kNm/kg, was reached when the pressing temperature was 290°C, the nip pressure about 8 MPa, the pressing time in the press nip 40 ms and the dwell time in contact with the steel belt 23.5 sec. It was also noted that no delamination occurred in these tests.In order to obtain both high dry and wet strength, it is important to have high lignin content, high temperature, high nip pressure and sufficiently long pressing time